high temperature dental castable refractory cement

Place of Origin:

Henan, China

Shape:

Powder

Material:

Clay,Alumina magnesia,Bauxite-mullite,Corundun

SiO2 Content (%):

15%-30%

Al2O3 Content (%):

45%-90%

MgO Content (%):

4.4%

CaO Content (%):

1.2-3.2%

Refractoriness (Degree):

Common (1580°< Refractoriness< 1770°)

CrO Content (%):

Appropriate

SiC Content (%):

Appropriate

Model Number:

customize

Brand Name:

Lite

Name:

high alumina self flowing refractory castable

Compressive strength 1000°C:

40-74Mpa

Compressive strength 1500°C:

43-150Mpa

Bending Strength 1000°C:

11-19Mpa

Bulk density(g/cm3):

2.3

Bending Strength 1500°C:

13-23Mpa

Reheating linear change 1000°C:

-0.02-+0.08

Reheating linear change 1500°C:

+0.10-+0.62

Max Service temperature °C ≥:

1650

Color:

White,Yellow,Grey Green etc